Method of imparting water repellency with non-fluorinated laundry treatment compositions

ABSTRACT

The present invention discloses a method of imparting water repellency and optionally stain release to fibrous substrates by contacting a fibrous substrate with a non-fluorinated laundry treatment composition inside a laundry machine. The laundry treatment composition contains a hydrophobic organic urethane compound having a urethane linkage and the residue of a substituted cyclic or acyclic sugar alcohol. Laundry additive compositions containing a first laundry treatment composition, having a hydrophobic organic urethane compound, and a second laundry treatment composition are also included.

FIELD OF INVENTION

This invention relates to a method of imparting water repellency andoptionally stain release to fibrous substrates by contacting a fibroussubstrate with a laundry treatment composition inside a laundry machine.

BACKGROUND OF THE INVENTION

Various compositions are known to be useful as treating agents toprovide water repellency and optionally stain release to textilesubstrates. Most textile treatments require industrial baths and curingequipment. Many such treating agents are fluorinated polymers andcopolymers, or non-fluorinated polymers and copolymers. Non-fluorinatedcompounds are predominately polyacrylate-based or urethane-basedcopolymers.

Fluorinated copolymers provide good repellency to water and oil. Suchpolymer compositions are commonly applied and cured at a fabric mill byindustrial methods. Various attempts have been made to produce anon-fluorinated water repellent, but previous non-fluorinated repellentcompounds have been less effective than the fluorinated counterparts.

Moore, in U.S. Pat. No. 6,864,312, discloses a polyurethane polymer thatprovides moisture resistance. Moore claims polyurethane polymer particledispersions, where the polyurethane polymers are isocyanate-terminatedprepolymers prepared from a formulation including a polyisocyanate and apolyol.

SUMMARY OF INVENTION

The need exists for a facile method of providing durable waterrepellency and optionally stain release to a fibrous substrate in ahome, laundering facility, or other small-scale setting, using commonlaundering equipment. Also desirable is a laundry treatment compositionthat provides similar or equivalent water repellency performance tofluorinated compositions that have been industrially applied to afibrous substrate. The present invention meets these needs.

The present invention comprises a method of imparting water repellencyand optionally stain release to fibrous substrates by contacting afibrous substrate with a non-fluorinated laundry treatment compositioninside a laundry machine. The laundry treatment composition comprises ahydrophobic organic urethane compound, the compound derived fromisocyanates and modified sugar alcohols. Laundry additive compositionscomprising a first laundry treatment composition, comprising ahydrophobic organic urethane compound, and a second laundry treatmentcomposition are also included.

The present invention relates to a method of imparting water repellencyand optionally stain release to fibrous substrates comprising contactinga fibrous substrate with a laundry treatment composition inside alaundry machine,

wherein the laundry treatment composition comprises a hydrophobiccompound having at least one linkage of Formula I:

—NHC(O)—X—  (I)

wherein

X is the residue of a cyclic or acyclic sugar alcohol which issubstituted with at least one —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; or mixtures thereof;

where the cyclic or acyclic sugar alcohol is selected from a saccharide,reduced sugar, aminosaccharide, aldonic acid, or aldonic acid lactone;

wherein

each n is independently 0 to 20;

each m is independently 0 to 20;

m+n is greater than 0;

each R¹ is independently a linear or branched alkyl group having 5 to 29carbons optionally comprising at least 1 unsaturated bond; and

each R² is independently —H or a linear, branched alkyl group having 6to 30 carbons optionally comprising at least 1 unsaturated bond, ormixtures thereof.

The present invention also relates to a laundry additive compositioncomprising a first laundry treatment composition and a second laundrytreatment composition which is different than the first laundrytreatment composition, where the first laundry treatment compositioncomprises a hydrophobic compound having at least one linkage of FormulaI as defined above.

DETAILED DESCRIPTION OF INVENTION

Herein all trademarks are designated with capital letters.

The present invention comprises a method of imparting water repellencyand optionally stain release to fibrous substrates by contacting afibrous substrate with a non-fluorinated laundry treatment compositioninside a laundry machine. Such a method provides the user the ability toenhance the performance and durability of water repellency tosubstrates, comparable to traditional industrially-applied fluorinatedcommercially available treatment agents, in a home, laundry facility, orother small-scale setting with the use of a laundry machine.

The present invention relates to a method of imparting water repellencyand optionally stain release to fibrous substrates comprising contactinga fibrous substrate with a laundry treatment composition inside alaundry machine, wherein the laundry treatment composition comprises ahydrophobic compound having at least one linkage of Formula (I):

—NHC(O)—X—  (I)

wherein X is the residue of a cyclic or acyclic sugar alcohol which issubstituted with at least one —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; or mixtures thereof; where thecyclic or acyclic sugar alcohol is selected from a saccharide, reducedsugar, aminosaccharide, aldonic acid, or aldonic acid lactone; whereineach n is independently 0 to 20; each m is independently 0 to 20; m+n isgreater than 0; each R¹ is independently a linear or branched alkylgroup having 5 to 29 carbons optionally comprising at least 1unsaturated bond; and each R² is independently —H, a linear or branchedalkyl group having 6 to 30 carbons optionally comprising at least 1unsaturated bond, or mixtures thereof. The term “residue of a cyclic oracyclic sugar alcohol” is herein defined as the molecular structure of acyclic or acyclic sugar alcohol when one or more H atoms has beenremoved from a hydroxyl group —OH. In Formula (I), the bond of X to—NHC(O)— forms a urethane functional group. The urethane functionalgroup may be formed by any suitable method, including by reacting anisocyanate, diisocyanate, or polyisocyanate with a cyclic or acyclicsugar alcohol which is substituted with at least one —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; —(CH₂CH₂O)_(n)(CH(CH₃)CHO)_(m)C(O)R¹;or mixtures thereof.

Preferably, the final compound contains 0% to about 1% of reactiveisocyanate groups. When optimum durable water repellency is desired, thelinkage of Formula (I) composes 80 to 100% by mol of the total urethanelinkages in the hydrophobic compound. In another embodiment, the linkageof Formula (I) composes 90 to 100% by mol of the total urethane linkagesin the hydrophobic compound. In a third embodiment, the linkage ofFormula (I) composes 95 to 100% by mol of the total urethane linkages inthe hydrophobic compound. In one embodiment, the molecular weight of thefinal compound is at least 10,000 g/mol.

The cyclic or acyclic sugar alcohol is selected from a saccharide,reduced sugar, aminosaccharide, aldonic acid, or aldonic acid lactone,and is substituted with at least one —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; or mixtures thereof. Such asubstitution lends hydrophobic character to the monomer, and to thepolymer molecules. In one embodiment, the cyclic or acyclic sugaralcohol is substituted with at least two —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; or mixtures thereof; and inanother embodiment, it is substituted with at least three —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; or mixtures thereof. Examples ofsuch sugar alcohols include but are not limited to aldoses and ketosessuch as those compounds derived from tetroses, pentoses, hexoses, andheptoses. Specific examples include glucose, glyceraldehyde, erythrose,arabinose, ribose, arabinose, allose, altrose, mannose, xylose, lyxose,gulose, glactose, talose, fructose, ribulose, mannoheptulose,sedohelptulose, threose, erythritol, threitol, glucopyranose,mannopyranose, talopyranose, allopyranose, altropyranose, idopyranose,gulopyranose, glucitol, mannitol, erythritol, sorbitol, arabitol,xylitol, ribitol, galactitol, fucitol, iditol, inositol,pentaerythritol, dipentaerythritol, volemitol, gluconic acid, glycericacid, xylonic acid, galactaric acid, ascorbic acid, citric acid,gluconic acid lactone, glyceric acid lactone, xylonic acid lactone,glucosamine, galactosamine, or mixtures thereof.

The cyclic or acyclic sugar alcohols are substituted with at least one—R¹; —C(O)R¹; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹ by any suitable method, includingesterification with a fatty acid, to form hydroxyl-functionalsubstituted sugar alcohols. In one embodiment, the fatty acidsubstitution of the cyclic or acyclic sugar alcohols has a melting pointof at least −59° C. In another embodiment, the fatty acid substitutionof the cyclic or acyclic sugar alcohols has a melting point of at least0° C., and in a third embodiment, the fatty acid substitution of thecyclic or acyclic sugar alcohols has a melting point of at least 40° C.Suitable fatty acids include, but are not limited to, caprylic acid,capric acid, lauric acid, mysteric acid, palmitic acid, stearic acid,arachidic acid, behenic acid, lignoceric acid, palmitoleic acid,lineolic acid, oleic acid, erucic acid, and mixtures thereof. In oneembodiment, R¹ is a linear or branched alkyl group having 11 to 29carbons, and in another embodiment, R¹ is a linear or branched alkylgroup having 17 to 21 carbons. In one embodiment, R² is a linear orbranched alkyl group having 12 to 30 carbons, in another embodiment, R²is a linear or branched alkyl group having 18 to 30 carbons, and inanother embodiment, R² is a linear or branched alkyl group having 18 to22 carbons.

In one embodiment, X is selected from Formulas (IIa), (IIb), or (IIc):

wherein each R is independently a direct bond to NHC(O) of Formula I;—H; —R¹; —C(O)R¹; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; each n is independently 0 to 20;each m is independently 0 to 20; m+n is greater than 0; r is 1 to 3; ais 0 or 1; p is independently 0 to 2; provided that a is 0 when r is 3;each R¹ is independently a linear or branched alkyl group having 5 to 29carbons optionally comprising at least 1 unsaturated bond; each R² isindependently —H, or a linear or branched alkyl group having 6 to 30carbons optionally comprising at least 1 unsaturated bond; or a mixturethereof, provided when the compound is Formula (IIa), then at least oneR is a direct bond to NHC(O) of Formula 1; and at least one R is a —R¹;—C(O)R¹; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; each R⁴ is independently a directbond to NHC(O) of Formula I; —H, a linear or branched alkyl group having6 to 30 carbons optionally comprising at least 1 unsaturated bond, orcombinations thereof; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; provided when the compound isFormula (IIb), then at least one R or R⁴ is a direct bond to NHC(O) ofFormula 1; and at least one R or R⁴ is a linear or branched alkyl groupoptionally comprising at least 1 unsaturated bond, or combinationsthereof; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; and each R¹⁹ is a direct bond toNHC(O) of Formula I; —H, —C(O)R¹, or —CH₂C[CH₂OR]₃, provided when thecompound is Formula (IIc), then at least one R¹⁹ or R is a direct bondto NHC(O) of Formula I; and at least one R¹⁹ or R is —C(O)R¹,—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹.

In Formulas (IIa), (IIb), or (IIc), the —(CH₂CH₂O)— representsoxyethylene groups (EO) and —(CH(CH₃)CH₂O)— represents oxypropylenegroups (PO). These compounds can contain only EO groups, only PO groups,or mixtures thereof. These compounds can also be present as a tri-blockcopolymer designated PEG-PPG-PEG (polyethylene glycol-polypropyleneglycol-polyethylene glycol), for example.

Where X is Formula (IIa), any suitable substituted reduced sugar alcoholmay be employed, including esters of 1,4-sorbitan, esters of2,5-sorbitan, and esters of 3,6-sorbitan. In one embodiment, X isselected from Formula (IIa) to be Formula (IIa′):

wherein R is further limited to independently a direct bond to NHC(O),—H; —R¹; or —C(O)R¹. In one embodiment, at least one R is —C(O)R¹ or R¹.Compounds used to form residues of Formula (IIa′), having at least oneof R is —H and at least one R is selected from —C(O)R¹, are commonlyknown as alkyl sorbitans. These sorbitans can be mono-substituted,di-substituted, or tri-substituted with —C(O)R¹. It is known thatcommercially available sorbitans, such as SPAN, contain a mixture of thevarious sorbitans ranging from where each R is H (un-substituted), andsorbitans where each R is —C(O)R¹ (fully substituted); wherein R¹ is alinear or branched alkyl group having 5 to 29 carbons; and mixtures ofvarious substitutions thereof. The commercially available sorbitans mayalso include amounts of sorbitol, isosorbide, or other intermediates orbyproducts.

In one embodiment, at least one R is —C(O)R¹, and R¹ is a linearbranched alkyl group having 5 to 29 carbons. In another embodiment, R¹is a linear or branched alkyl group having 7 to 21 carbons, and in athird embodiment, R¹ is a linear or branched alkyl group having 11 to 21carbons. Preferred compounds used to form these residues include mono-,di-, and tri-substituted sorbitans derived from caprylic acid, capricacid, lauric acid, mysteric acid, palmitic acid, stearic acid, arachidicacid, behenic acid, lignoceric acid, and mixtures thereof. Particularlypreferred compounds used to form X include mono-, di-, andtri-substituted sorbitan stearates or sorbitan behenins.

Optionally, R¹ is a linear or branched alkyl group having 5 to 29carbons comprising at least 1 unsaturated bond. Examples of compoundsused to form residues of Formula (IIa′) wherein at least one R isselected from —C(O)R¹; and R¹ contains least 1 unsaturated bond,include, but are not limited to, sorbitan trioleate (i.e., wherein R¹ is—C₇H₁₄CH═CHC₈H₇). Other examples include but are not limited to mono-,di-, and tri-substituted sorbitans derived from palmitoleic acid,lineolic acid, arachidonic acid, and erucic acid.

In one embodiment, X of Formula (IIa′) is employed, wherein R is furtherlimited to independently a direct bond to NHC(O), —H;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹. In this embodiment, at least oneR is independently —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R² or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹. Compounds forming X of Formula(IIa′), wherein at least one R is —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R² or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹, wherein each m is independently 0to 20, each n is independently 0 to 20, and n+m is greater than 0 areknown as polysorbates and are commercially available under the tradenameTWEEN. These polysorbates can be mono-substituted, di-substituted, ortri-substituted with alkyl groups R¹ or R². It is known thatcommercially available polysorbates, contain a mixture of the variouspolysorbates ranging from where each R² is H (unsubstituted), andpolysorbates where each R¹ is a linear or branched alkyl group having 5to 29 carbons (fully substituted); and mixtures of various substitutionsthereof. Examples of compounds used to form X of Formula (IIa′) includepolysorbates such as polysorbate tristearate, and polysorbatemonostearate. Examples of compounds used to form X of Formula (IIa′)wherein m+n is greater than 0, and wherein R¹ comprises at least 1unsaturated bond, include but are not limited to, polysorbate trioleate(wherein R¹ is C₇H₁₄CH═CHC₈H₇), are sold commercially under the namePolysorbate 80. Reagents may include mixtures of compounds havingvarious values for R, R¹, and R², and may also include mixtures ofcompounds where R¹ comprises at least one unsaturated bond withcompounds where R¹ is fully saturated. In one aspect, R² is H and m is apositive integer.

In one embodiment, X is selected from Formula (IIb). Compounds used toform X of Formula (IIb) are known as alkyl citrates. These citrates canbe present as a mono-substituted, di-substituted, or tri-substitutedcompound with alkyl groups. It is known that commercially availablecitrates contain a mixture of the various citrates as well as citricacids from where R and each R⁴ is —H, ranging to citrates where each R⁴is a linear or branched alkyl group having 6 to 30 carbons optionallycomprising at least 1 unsaturated bond; and mixtures of varioussubstitutions thereof. Mixtures of citrates having various values forR¹, R², and R⁴ may be used, and may also include mixtures of compoundswhere R¹ comprises at least one unsaturated bond with compounds where R¹is fully saturated. Alkyl citrates are also commercially availablewherein m+n is greater than 0, R⁴ is —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;or —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹ and are present in the varioussubstitutions from wherein R and each R² is H to wherein each R¹ and/orR² is a linear or branched alkyl group having 5 to 30 carbons optionallycomprising at least 1 unsaturated bond. Examples of compounds used toform X of Formula (IIb) include, but are not limited to, trialkylcitrates.

In one embodiment, X is selected from Formula (IIc). Compounds used toform X of Formula (IIc) are known as pentaerythriol esters. Thesepentaerythriol esters can be present as a mono-substituted,di-substituted, or tri-substituted with alkyl groups. Preferredcompounds used to form X of Formula (IIc) are dipentaerythriol esters,where R¹⁹ is —CH₂C[CH₂OR]₃. It is known that commercially availablepentaerythriol esters contain a mixture of the various pentaerythriolesters where R¹⁹ and each R is —H, ranging to pentaerythriol esterswhere each R is —C(O)R¹, and R¹ is a linear or branched alkyl grouphaving 5 to 29 carbons optionally comprising at least 1 unsaturatedbond; and mixtures of various substitutions thereof. The pentaerythriolesters also may contain compounds with mixtures of different chainlengths for R, or mixtures of compounds where R¹ comprises at least oneunsaturated bond with compounds where R¹ is fully saturated.

Residue X of Formulas (IIa), (IIb), and (IIc) can all be bio-basedderived. By “bio-based derived”, it is meant that at least 10% of thematerial can be produced from non-crude oil sources, such as plants,other vegetation, and tallow. In one embodiment, X is from about 10% to100% bio-based derived. In one embodiment, X is from about 35% to 100%bio-based derived. In another embodiment, X is from about 50% to 100%bio-based derived. In one embodiment, X is from about 75% to 100%bio-based derived. In one embodiment, X is 100% bio-based derived. Theaverage OH value of the substituted sugar alcohol compounds used to formX can range from just greater than 0 to about 230. In one embodiment,the average OH value is from about 10 to about 175, and in anotherembodiment, the average OH value is from about 25 to about 140.

In one embodiment, the hydrophobic compound further comprises at leastone moiety Q to form Formula (I′):

-Q-NHC(O)—X—  (I′)

where Q is a monovalent, divalent, or polyvalent moiety selected fromlinear or branched, cyclic or acyclic, alkylene groups optionallycontaining at least one group selected from alkoxy, phenyl, siloxane,urethane, urea, biuret, uretdione, cyclized isocyanate, allophanate, orisocyanurate. Moiety Q can be formed from an isocyanate, diisocyanate,or polyisocyanate compound. In one embodiment, Q is the residue of anisocyanate, diisocyanate, or polyisocyanate, herein defined as themolecular structure of an isocyanate, diisocyanate, or polyisocyanatewhere all isocyanate groups NCO have been removed. For example, onemethod of making the compounds of the present invention includesreacting a substituted sugar alcohol compound, or mixtures thereof, withan isocyanate group-containing compound selected from an isocyanate,diisocyanate, polyisocyanate, or mixture thereof. Where multipleisocyanate groups are present, the isocyanate group-containing compoundadds to the branched nature of the polymer. The term “polyisocyanate” isdefined as di- and higher-functional isocyanates, and the term includesoligomers. Any monoisocyanate or polyisocyanate having predominately twoor more isocyanate groups, or any isocyanate precursor of apolyisocyanate having predominately two or more isocyanate groups, issuitable for use in this invention. For example, hexamethylenediisocyanate homopolymers are suitable for use herein and arecommercially available. In this case, Q would be a linear C₆ alkylenehaving cyclized isocyanate groups. It is recognized that minor amountsof diisocyanates can remain in products having multiple isocyanategroups. An example of this is a biuret containing residual small amountsof hexamethylene diisocyanate.

Also suitable for use as the polyisocyanate reactant are hydrocarbondiisocyanate-derived isocyanurate trimers, where Q is a trivalent linearalkylene having an isocyanurate group. Preferred is DESMODUR N-100 (ahexamethylene diisocyanate-based compound available from BayerCorporation, Pittsburgh, Pa.). Other triisocyanates useful for thepurposes of this invention are those obtained by reacting three moles oftoluene diisocyanate, where Q is a trivalent polyaromatic ring structurehaving a cyclized isocyanate group. The isocyanurate trimer of toluenediisocyanate and that of 3-isocyanatomethyl-3,4,4-trimethylcyclohexylisocyanate are other examples of triisocyanates useful for the purposesof this invention, as is methane-tris-(phenylisocyanate). Precursors ofpolyisocyanate, such as diisocyanate, are also suitable for use in thepresent invention as substrates for the polyisocyanates. DESMODURN-3300, DESMODUR N-3600, DESMODUR Z-4470, DESMODUR H, DESMODUR N3790,and DESMODUR XP 2410, from Bayer Corporation, Pittsburgh, Pa., andbis-(4-isocyanatocylohexyl)methane are also suitable in the invention.

Preferred polyisocyanate reactants are the aliphatic and aromaticpolyisocyanates containing biuret structures, or polydimethyl siloxanecontaining isocyanates. Such polyisocyanates can also contain bothaliphatic and aromatic substituents.

Preferred as the (poly)isocyanate reactant for all the embodiments ofthe invention herein are hexamethylene diisocyanate homopolymerscommercially available, for instance as DESMODUR N-100, DESMODUR N-75and DESMODUR N-3200 from Bayer Corporation, Pittsburgh, Pa.;3-isocyanatomethyl-3,4,4-trimethylcyclohexyl isocyanate available, forinstance as DESMODUR I (Bayer Corporation);bis-(4-isocyanatocylohexyl)methane available, for instance as DESMODUR W(Bayer Corporation) and diisocyanate trimers of formulas:

The diisocyanate trimers (Va-e) are available, for instance as DESMODURZ4470, DESMODUR IL, DESMODUR N-3300, DESMODUR XP2410, and DESMODUR N100,respectively, from Bayer Corporation. In one embodiment, Q is selectedfrom Formulas (IIIa), (IIIb), (IIIc), (IIId), or (IIIe):

In one embodiment, the hydrophobic compound further comprises at leastone linkage selected from Formulas (IVa), (IVb), (IVc), or mixturesthereof:

R⁶-D  (IVa),

R¹⁵—(OCH₂CH(OR¹⁶)CH₂)_(z)—OR¹⁷  (IVb),

—NH—C(O)—NH—X  (IVc)

wherein D is selected from —N(R¹²)—C(O)—NH—, —OC(O)NH—, —C(O)NH—,—SC(O)NH—, —O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—C(O)NH—, or—[C(O)]—O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—C(O)NH—; X is defined as above;R⁶ is selected from a —C₁ to C₃₀ linear or branched alkyl optionallycomprising at least one unsaturated group, a hydroxy- orurethane-functional C₁ to C₃₀ linear or branched alkyl, a hydroxy- orurethane-functional linear or branched C₁ to C₃₀ polyether, a hydroxy-or urethane-functional linear or branched polyester having a polyesterpolymer backbone, a hydroxy- or urethane-functional linear or branchedorganosiloxane, an amine- or urea-functional linear or branchedorganosiloxane, a thiol- or thiocarbonate functional C₁ to C₃₀ linear orbranched alkyl, an amine- or urea-functional C₁ to C₃₀ linear orbranched alkyl,

wherein R⁷, R⁸, and R⁹ are each independently, —H, —C₁ to C₆ alkyl, orcombinations thereof; R¹⁰ is a divalent alkyl group of 1 to 20 carbons;R¹² is —H or a monovalent C₁ to C₆ alkyl group; R¹⁵, R¹⁶, and R¹⁷ areeach independently a —H, —C(O)NH—, —R¹⁸; or —C(O)R¹⁸ provided that atleast one R¹⁵, R¹⁶, or R¹⁷ is a —C(O)NH—; R¹⁸ is independently a linearor branched alkyl group having 5 to 29 carbons optionally comprising atleast 1 unsaturated bond; z is 1 to 15; Y is Cl; s is an integer of 0 to50; t is an integer of 0 to 50; and s+t is greater than 0. Such alinkage may be formed by reacting active isocyanate groups with anotherisocyanate-reactive compound selected from water, organic compounds ofFormula (VIa)

R⁵-A  (VIa), or

organic compounds of Formula (VIb)

R³—(OCH₂CH(OR³)CH₂)_(z)—OR³  (VIb),

or mixtures thereof, wherein R⁵ is selected from a —C₁ to C₃₀ linear orbranched alkyl optionally comprising at least one unsaturated group, ahydroxy-functional C₁ to C₃₀ linear or branched alkyl, ahydroxy-functional linear or branched C₁ to C₃₀ polyether, ahydroxy-functional linear or branched polyester having a polyesterpolymer backbone, a hydroxy-functional linear or branchedorganosiloxane, an amine-functional linear or branched organosiloxane, athiol-functional C₁ to C₃₀ linear or branched alkyl, an amine-functionalC₁ to C₃₀ linear or branched alkyl,

A is selected from —N(R¹²)H, —OH, —COOH, —SH,—O—(CH₂CH₂O)_(s)(CH(CH₃CH₂O)_(t)—H, or(C(O)—O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)H; R³ is independently selectedfrom —H; —R¹⁸; or —C(O)R¹⁸, provided that at least one R³ is —H; z isdefined as above; R¹² is defined as above; R¹⁸ is defined as above; ands and t are defined as above. The term “branched”, as used herein, meansthat the functional chain can be branched at any point, for example as aquaternary substituted carbon, and can contain any number of branchedsubstitutions.

When optimum stain release is desired, for example, the compoundselected from Formula (VIa), (VIb), or water reacts with about 0.1 mol %to about 70 mol % of reactive isocyanate groups, and the substitutedsugar alcohols react with about 30 mol % to about 99.9 mol % of reactiveisocyanate groups, to form a urethane compound where about 30 mol % toabout 99.9 mol % of total urethane linkages present in the compound fitFormula (I) and about 0.1 mol % to about 70 mol % of total reactiveisocyanate groups present fit one or more of Formulas (IVa), (IVb), or(IVc). In another embodiment, the compound selected from Formula (VIa),(VIb), or water reacts with about 40 mol % to about 70 mol % of reactiveisocyanate groups, and the substituted sugar alcohols react with about30 mol % to about 60 mol % of reactive isocyanate groups, to form aurethane compound where about 30 mol % to about 60 mol % of totalurethane linkages present in the compound fit Formula (I) and about 40mol % to about 70 mol % of total reactive isocyanate groups present fitone or more of Formulas (IVa), (IVb), or (IVc). Preferably the number oflinkages of Formula (I) is greater than the sum of linkages of Formulas(IVa), (IVb), and (IVc).

In one embodiment, the linkage of Formula (IVc) is present in thehydrophobic compound. Such a linkage is a urea functional group and canbe formed from reacting water with active isocyanate groups in thecompound. In a further embodiment, the linkage of Formula (IVa) ispresent, where D is —O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—C(O)NH—, or—[C(O)]—O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—C(O)NH—. Such a linkage may beformed by reacting a compound of Formula (VIa). Such a compound can be ahydrophilic water-solvatable material comprising at least onehydroxy-terminated polyether of Formula (VIa) whereinisocyanate-reactive group A is —O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—H or—[C(O)]—O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—H. In this embodiment,—(CH₂CH₂O)— represents oxyethylene groups (EO) and —(CH(CH₃)CH₂O)—represents oxypropylene groups (PO). These polyethers can contain onlyEO groups, only PO groups, or mixtures thereof. These polyethers canalso be present as a tri-block copolymer designated PEG-PPG-PEG(polyethylene glycol-polypropylene glycol-polyethylene glycol).Preferably, the polyethers are the commercially availablemethoxypolyethylene glycols (MPEG's), or mixtures thereof. Alsocommercially available, and suitable for the preparation of thecompositions of the present invention, are butoxypolyoxyalkylenescontaining equal amounts by weight of oxyethylene and oxypropylenegroups (Union Carbide Corp. 50-HB Series UCON Fluids and Lubricants) andhaving an average molecular weight greater than about 1000. In oneaspect, the hydroxy-terminal polyethers of Formula (VIa) have an averagemolecular weight equal to or greater than about 200. In another aspect,the average molecular weight is between 350 and 2000.

In another embodiment, the linkage of Formula (IVa) is present, where Dis —N(R¹²)—C(O)—NH—, —OC(O)NH—, —C(O)NH—, or —SC(O)NH—. Such a linkagemay be formed from an organic compound of Formula (VIa), whereisocyanate-reactive group A is —OH, —C(O)OH, —SH, or —NH(R¹²); and R⁵ isselected from a —C₁ to C₃₀ linear or branched alkyl optionallycomprising at least one unsaturated group, a hydroxy-functional C₁ toC₃₀ linear or branched alkyl, a hydroxy-functional linear or branched C₁to C₃₀ polyether, a hydroxy-functional linear or branched polyesterhaving a polyester polymer backbone, a hydroxy- or amine-functionallinear or branched organosiloxane, a thiol-functional C₁ to C₃₀ linearor branched alkyl, an amine-functional C₁ to C₃₀ linear or branchedalkyl.

Where D is —OC(O)NH— or A is —OH, examples of Formula (VIa) include butare not limited to alkyl alcohols such as propanol, butanol, or fattyalcohols including stearyl alcohol (R⁵ is a —C₁ to C₃₀ linear orbranched alkyl optionally comprising at least one unsaturated group);alkyl diols or polyols such as ethanediol, propanediol, butanediol, orhexanediol (R⁵ is a hydroxy-functional C₁ to C₃₀ linear or branchedalkyl); alkylene glycol ethers such as triethylene glycol, tetraethyleneglycol, poly(ethylene glycol) (PEG), poly(propylene glycol) (PPG),poly(tetrahydrofuran), or glycol ethers having mixtures of PEG, PPG, orTHF units (R⁵ is a hydroxy-functional linear or branched C₁ to C₃₀polyether); polyester polyols (R⁵ is a hydroxy-functional linear orbranched polyester having a polyester polymer backbone); siliconeprepolymer polyols (R⁵ is a hydroxy-functional linear or branchedorganosiloxane); N,N-dimethylaminoethanol (R⁵ is an amine-functional C₁to C₃₀ linear or branched alkyl); choline chloride or betaine HCl (R⁵ isY⁻(R⁷)(R⁸)(R⁹)N⁺R¹⁰—); butanone oxime (R⁵ is (R⁷)(R⁸)C═N—). Thepolyether polyols can contain only EO groups, only PO groups, only THFgroups, or mixtures thereof. These polyethers can also be present as ablock copolymer, such as that designated by PEG-PPG-PEG (polyethyleneglycol-polypropylene glycol-polyethylene glycol). In one aspect, thepolyether glycols have an average molecular weight equal to or greaterthan about 200. In another aspect, the average molecular weight isbetween 350 and 2000.

Where D is —C(O)NH— or A is —COOH, examples of Formula (VIa) include butare not limited to fatty acids such as caprylic acid, capric acid,lauric acid, mysteric acid, palmitic acid, stearic acid, arachidic acid,behenic acid, lignoceric acid, palmitoleic acid, lineolic acid,arachidonic acid, oleic acid, or erucic acid (R⁵ is a —C₁ to C₃₀ linearor branched alkyl optionally comprising at least one unsaturated group);hydroxy-containing acids such as hydroxycaprylic acid, hydroxycapricacid, hydroxylauric acid, hydroxymysteric acid, hydroxypalmitic acid,hydroxystearic acid, hydroxyarachidic acid, hydroxybehenic acid,hydroxylignoceric acid, hydroxypalmitoleic acid, hydroxylineolic acid,hydroxyarachidonic acid, hydroxyoleic acid, or hydroxyerucic acid (R⁵ isa hydroxy-functional C₁ to C₃₀ linear or branched alkyl); andmercaptoalkanoic acids such as mercaptopropionic acid (R⁵ is athiol-functional C₁ to C₃₀ linear or branched alkyl).

Where D is —SC(O)NH— or A is —SH, specific examples of Formula (VIa)include but are not limited to alkyl thiols such as lauryl mercaptan ordodecyl mercaptan (R⁵ is a —C₁ to C₃₀ linear or branched alkyloptionally comprising at least one unsaturated group). Where D is—N(R¹²)—C(O)—NH— or A is —NH(R¹²), specific examples of Formula (VIa)include but are not limited to alkyl amines such as diisopropylamine,propylamine, hexylmine, or laurylamine (R⁵ is a —C₁ to C₃₀ linear orbranched alkyl optionally comprising at least one unsaturated group);alkanolamines such as ethanolamine or propanolamine (R⁵ is ahydroxy-functional C₁ to C₃₀ linear or branched alkyl); siliconeprepolymer polyamines (R⁵ is a amine-functional linear or branchedorganosiloxane); alkyl diamines (R⁵ is an amine-functional C₁ to C₃₀linear or branched alkyl); and aminoalkanesulfonic acids such as2-aminoethanesulfonic acid (R⁵ is HO—S(O)₂R¹⁰—).

In a further embodiment, the hydrophobic compound comprises a linkage ofFormula (IVb). Such linkages may be formed by the reaction of activeisocyanate groups with a compound of Formula (VIb). These compounds arecommonly referred to as polyglycerols. These polyglycerols can bepresent where R³ is independently a —H; —R¹⁸; —C(O)R¹⁸ provided that atleast one R³ is a —H; and wherein R¹⁸ is independently a linear orbranched alkyl group having 5 to 29 carbons optionally comprising atleast 1 unsaturated bond. Specific examples include but are not limitedto triglycerol monostearate, triglycerol distearate, hexaglycerolmonostearate, hexaglycerol distearate, decaglycerylmono(carpylate/caprate), decaglyceryl di(carpylate/caprate),decaglycerol, polyglycerol-3, and C18 diglyceride.

In one embodiment, the hydrophobic compound comprises more than one typeof linkages selected from Formulas (IVa), (IVb), and (IVc). In additionto compounds of the present invention as described herein, thesecompositions may also comprise additional compounds that are presentfrom commercially available sorbitans, polysorbates, alkyl citrates, orpentaethritols. These compounds can be present as a mixture of thevarious substituted sugar alcohols from fully unsubstituted to fullysubstituted, and the various substitutions in between, and optionally,the linear or branched alkyl group having 5 to 29 carbons comprises atleast 1 unsaturated bond.

The laundry treatment compositions comprise the hydrophobic compound butmay further comprise a solvent selected from organic solvents or water,such that the laundry treatment composition is in the form of asolution, an aqueous emulsion, or an aqueous dispersion.

In one embodiment, the laundry treatment composition further comprises awax. The wax component includes any of a variety of known waxes,preferably used in a weight ratio of laundry additive composition:waxfrom about 1:10 to about 10:1. In one aspect, the ratio ranges fromabout 1:8 to about 8:1, and in another aspect, the ratio ranges fromabout 2:8 to about 8:2. The melting point of the wax is greater thanabout 30° C. In one aspect, the melting point is greater than about30-70° C., and in another aspect, the melting point is greater thanabout 40-55° C. Examples include animal waxes, plant and vegetablewaxes, mineral waxes, petroleum waxes, and synthetic waxes, includingsilicone waxes. More specifically, the wax is selected from beeswax;microcrystalline wax; oxidized microcrystalline wax; paraffin wax;montan wax; ozokerite wax; carnauba wax; candililla wax; palm wax; whalewax; lanolin; sugar cane wax; sugar esters; polyolefin wax; mono-, di,or tri-glyceride esters; fatty acid ester waxes; or blends thereof. Inanother embodiment, the wax is selected from silicone wax, a blend ofsilicone waxes, or a blend of silicone wax with at least onenon-silicone wax.

Of particular interest are mono-, di-, or tri-glyceride ester waxestypically found in the food and cosmetics industries. Such compounds canbe biological unmodified alkyl esters but also include mono- ordi-glycerides modified with reactive compounds including fatty acids oracetic acid. Typically, these compounds are mixtures of compoundscontaining mono-substituted, di-substituted, and tri-substituted estersof a distribution of chain lengths. Similarly, other polyfunctionalalcohols may be esterified with fatty acids to make suitable, functionalwaxes. Particularly preferred ester compounds include but are notlimited to beeswax, candililla wax, carnauba wax, surgarcane wax, palmwax, tribehenin, fatty acid triglycerides, fatty acid glycol esters,acetic esters of monoglycerides, and blends thereof. Such estercompounds are available from Croda, East Yorkshire, England; or DuPontNutrition & Health, Copenahgen, Denmark.

A variety of silicone waxes may be employed in the invention, includingbut not limited to alkyl silicones, alkyl aryl silicones, and blendsthereof. Particularly preferred are alkylated silicones based on alkylpendant groups, including those compounds of Formula (IV).

Such compounds range from liquids to soft pastes to hard waxes, and thephysical properties can be tailored by varying the molecular weight,alkyl chain lengths, and long alkyl chain content. Preferably, g is 2 to40. In another aspect, g is 10 to 32, and in another aspect, g is 18 to32. Variables d and e are independently 2 to 20. In one aspect, d and eare independently 2 to 10, and in another aspect, d and e areindependently 2 to 6. The ratio of silicone to alkyls and the chainlength of the alkyls determine the melting point and liquidity of thefinal product. Examples of suitable compounds include DOW CORNING waxesavailable from Dow Corning, Midland, Mich.; WACKER silicone waxesavailable from, Wacker, Munchen, Germany; silicone waxes available fromMomentive Specialty Chemicals, Inc., Columbus, Ohio; and SILWAX,available from Siltech, Toronto, Canada.

The laundry treatment compositions can be made in one step. The laundrytreatment compositions comprising products of more than one substitutedsugar alcohol residue and/or one or more linkages of Formulas (IVa),(IVb), and (IVc) can be also made in one step. In one embodiment, ifmore than one substituted sugar alcohol residue and/or one or morelinkages of Formulas (IVa), (IVb), and (IVc) are present, then thesynthesis can be completed sequentially. A sequential addition isespecially useful when employing substituted sugar alcohols with high OHnumbers, or when using polyfunctional compounds of Formulas (VIa) or(VIb). These steps comprise reacting (a) at least one isocyanategroup-containing compound selected from isocyanate, diisocyanate,polyisocyanate, or mixtures thereof, and (b) at least one substitutedsugar alcohol. When a second compound is used selected from water,Formula (VIa), or Formula (VIb), molar concentrations of the at leastone substituted sugar alcohol are such that there remains unreactedisocyanate groups to react with the one or more compounds selected fromwater, Formula (VIa), or Formula (VIb).

This reaction is typically conducted by charging a reaction vessel withthe isocyanate, diisocyanate, or polyisocyanate, and at least onesubstituted sugar alcohol, and optionally a second compound selectedfrom water, Formula (VIa), or Formula (VIb). The order of reagentaddition is not critical, but if water is used, the water should beadded after the isocyanates and at least one substituted sugar alcoholare reacted.

The specific weight of the reactants charged is based on theirequivalent weights and on the working capacity of the reaction vessel,and is adjusted so that substituted sugar alcohol will be consumed inthe first step. A suitable dry organic solvent free ofisocyanate-reactive groups is typically used as a solvent. Ketones arethe preferred solvents, and methylisobutylketone (MIBK) is particularlypreferred for convenience and availability. The charge is agitated, andtemperature adjusted to about 40° C. to 70° C. Typically, a catalystsuch as iron(III) chloride in an organic solvent is then added,typically in an amount of from about 0.01 to about 1.0 weight % based onthe dry weight of the composition, and the temperature is raised toabout 80° C. to 100° C. A co-catalyst, such as sodium carbonate, mayalso be used. If water is to be added, the initial reaction is conductedso that less than 100% of the isocyanate groups are reacted. In thesecond step after holding for several hours, additional solvent, water,and optionally a second compound are added. In one embodiment, and themixture is allowed to react for several more hours or until all of theisocyanate has been reacted. In the process of preparing the aqueoussolutions or dispersions of the laundry treatment compositions,additional water can then be added along with surfactants, if desired,to the urethane compounds and stirred until thoroughly mixed. Followinga homogenization or sonification step, the organic solvent can beremoved by evaporation at reduced pressure, and the remaining aqueoussolution or dispersion of the compound of the present invention can beused as is or subjected to further processing.

It will be apparent to one skilled in the art that many changes to anyor all of the above procedures can also be used to optimize the reactionconditions for obtaining maximum yield, productivity, or productquality.

In another embodiment, the present invention is a laundry additivecomposition comprising a first laundry treatment composition and asecond laundry treatment composition which is different than the firstlaundry treatment composition, where the first laundry treatmentcomposition comprises a hydrophobic compound having at least one linkageof Formula I:

NHC(O)—X—  (I)

wherein X is the residue of a cyclic or acyclic sugar alcohol which issubstituted with at least one —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; where the cyclic or acyclic sugaralcohol is selected from a saccharide, reduced sugar, aminosaccharide,aldonic acid, or aldonic acid lactone; wherein each n is independently 0to 20; each m is independently 0 to 20; m+n is greater than 0; each R¹is independently a linear or branched alkyl group having 5 to 29 carbonsoptionally comprising at least 1 unsaturated bond; each R² isindependently —H, a linear or branched alkyl group having 6 to 30carbons optionally comprising at least 1 unsaturated bond, or mixturesthereof. This laundry additive composition can be formed by adding thecomponents separately to the laundry machine on-site, or the firstlaundry treatment composition can be pre-mixed with the second laundrytreatment composition. In one embodiment, the total hydrophobic compoundcontent (solids content) from the first laundry treatment compositioncomposes from about 10% to about 40% by weight of the total laundryadditive composition, and from about 2% to 30% by weight of the laundryliquor. In another embodiment, the total hydrophobic compound content(solids content) from the first laundry treatment composition composesfrom about 15% to about 25% by weight of the total laundry additivecomposition.

In one embodiment, the second laundry treatment composition is a laundrydetergent composition, fabric softener composition, wrinkle releaseagent, stain release agent, bleaching agent, color brightening agent, ormixtures thereof. Other additives commonly used with such treatingagents or finishes are also optionally present, such as surfactants,emulsifiers, pH adjusters, silicones, soil release agents, crosslinkers, wetting agents, wax extenders, antistatic agents, fragrances,antimicrobials and preservatives, dyes and colorants, viscosity controlagents, antioxidants and sunscreen materials, pearlizing and opacifyingagents, dye transfer inhibitors and dye fixatives, chlorine scavengers,electrolytes, enzymes, and other additives known by those skilled in theart. Suitable surfactants include anionic, cationic, nonionic, N-oxidesand amphoteric surfactants. Examples of such additives includeprocessing aids, foaming agents, lubricants, anti-stains, and the like.

Such additional components comprise compounds or compositions thatprovide surface effects such as no iron, easy to iron, shrinkagecontrol, wrinkle free, permanent press, moisture control, softness,strength, anti-slip, anti-static, anti-snag, anti-pill, stain release,soil repellency, soil release, water repellency, odor control,antimicrobial, sun protection, cleanability and similar effects. One ormore of such treating agents or finishes are applied to the substratebefore, after, or simultaneously with the composition of the presentinvention. For example, for fibrous substrates, when synthetic or cottonfabrics are treated, use of a wetting agent can be desirable, such asALKANOL 6112 available from E. I. du Pont de Nemours and Company,Wilmington, Del. When cotton or cotton-blended fabrics are treated, awrinkle-resistant resin can be used such as PERMAFRESH EFC availablefrom Omnova Solutions, Chester, S.C.

Optionally, a blocked isocyanate is added with the composition of thepresent invention to further promote durability (i.e., as a blendedcomposition). An example of a suitable blocked isocyanate to use in thepresent invention is PHOBOL XAN available from Huntsman Corp, Salt LakeCity, Utah Other commercially available blocked isocyanates are alsosuitable for use herein. The desirability of adding a blocked isocyanatedepends on the particular application for the copolymer. For most of thepresently envisioned applications, it does not need to be present toachieve satisfactory cross-linking between chains or bonding to thesubstrate. When added as a blended isocyanate, amounts up to about 20%by weight are added.

The method of imparting water repellency and optionally stain release tofibrous substrates comprising contacting a fibrous substrate with alaundry treatment composition inside a laundry machine can be practicedby any suitable method. Preferably, water is used to help disperse thelaundry treatment composition, such as by a wash cycle or rinse cycle ofthe laundry machine. The water temperature used in the wash cycle orrinse cycle may be any temperature including cold, room temperature,warm, or hot. Methods of contacting the additive with the substrateinclude, but are not limited to, introducing the laundry treatmentcomposition by pouring the treatment composition into the basin of thelaundry machine, pouring the treatment composition into a detergent ortreating agent reservoir of the laundry machine, adding a dissolvablepouch containing the additive composition, or adding acontrolled-release reusable container containing the additivecomposition. Any of the above methods may also be employed using alaundry additive composition comprising two laundry treatmentcompositions. Alternatively, the laundry additive composition or laundrytreatment composition may be introduced into an aqueous liquor andcontacted with a fibrous substrate into a tub, bucket or sink, such aswhen washing fabrics by hand.

In one embodiment, the laundry treatment composition or laundry additivecomposition is poured into the wash basin, or into a detergent ortreating agent reservoir, of the laundry machine and the machine isprogrammed to run a wash cycle or rinse cycle. In one embodiment, thewash basin is partially filled with water, the laundry treatmentcomposition or laundry additive composition is poured into the water,and the water is allowed to fill the wash basin. Detergent is thenoptionally added, the fibrous substrate is added to the wash basin, andthe laundry machine is allowed to run a full wash or rinse cycle.

In one embodiment, the method further comprises a step of curing thehydrophobic compound with heat. Any suitable heating method may be used,such as machine drying in a dryer, ironing, steaming, blow drying,drying under a heat lamp, or drying near a radiative source of heat. Inone embodiment, the cure step occurs at a temperature of about 30° C. toabout 100° C. In another embodiment, the cure step occurs at atemperature of about 35° C. to about 80° C., and in another embodimentthe temperature is about 40° C. to about 60° C., for a time of at least30 minutes, preferably at least 35 minutes, and more preferably at least40 minutes. Any drying method can be practiced, including air drying,tumbling dry, or heating the substrate to dryness. Such drying cyclesare commonly found on clothes drying machines, including a tumble drycycle, a tumble dry with heat cycle, or a heated non-tumble cycle. Inone embodiment, the treated substrate is tumbled dry with heat. Suchcuring enhances oil-, water- and soil repellency and durability of therepellency. While these curing conditions are typical, some commercialapparatus may operate outside these ranges because of its specificdesign features.

The compound or composition of the present invention is applied to thesubstrate individually, or in combination with other optional textilefinishes or surface treating agents. Such optional additional componentsinclude treating agents or finishes to achieve additional surfaceeffects, or additives commonly used with such agents or finishes.

In another embodiment, the present invention is a fibrous substrate madeby the process as disclosed above. The present invention furthercomprises substrates treated with a compound or composition of thepresent invention as described above. Suitable substrates includefibrous substrates. The fibrous substrates include fibers, yarns,fabrics, fabric blends, textiles, nonwovens, paper, leather, andcarpets. These are made from natural or synthetic fibers includingcotton, cellulose, wool, silk, rayon, nylon, aramid, acetate, acrylic,jute, sisal, sea grass, coir, polyamide, polyester, polyolefin,polyacrylonitrile, polypropylene, polyaramid, or blends thereof. By“fabric blends” is meant fabric made of two or more types of fibers.Typically these blends are a combination of at least one natural fiberand at least one synthetic fiber, but also can include a blend of two ormore natural fibers or of two or more synthetic fibers. The nonwovensubstrates include, for example, spunlaced nonwovens, such as SONTARAavailable from E. I. du Pont de Nemours and Company, Wilmington, Del.,and spunbonded-meltblown-spunbonded nonwovens. The treated substrates ofthe present invention have excellent water repellency and optionallystain release properties.

Test Methods and Materials

All solvents and reagents, unless otherwise indicated, were purchasedfrom Sigma-Aldrich, St. Louis, Mo., and used directly as supplied.

Sorbitan tristearate is commercially available from Croda, EastYorkshire, England, or DuPont Nutrition & Health, Copenhagen, Denmark.Sorbitan tribehenin 50 was obtained from DuPont Nutrition & Health,Copenhagen, Denmark. Stearyl pentaerythritol is commercially availablefrom DuPont Nutrition & Health, Copenhagen, Denmark. Tri(2-octadodecyl)citrate is commercially available from Lubrizol, Wickliffe, Ohio.

DESMODUR N-100 was obtained from Bayer Corporation, Pittsburgh, Pa.

PHOBOL XAN was obtained from Huntsman Corp, Salt Lake City, Utah.

SILWAX D226 and SILWAX E1316 are alkylated silicone waxes available fromSiltech Corporation, Toronto, Canada.

CHEMIDEX S is a stearamidopropyl dimethylamine surfactant available fromLubrizol, Wickliffe, Ohio.

ETHAL LA-4 is an ethoxylated emulsifier available from Ethox Chemicals,Greenville, S.C.

WITCO C-6094 is a modified alpha olefin sulfonate surfactant availablefrom AkzoNobel, Chicago, Ill.

WACKER SRE is a silicone emulsifier, and WACKER W23 is apolymethylsiloxane wax, both available from Wacker Chemie AG, München,Germany.

DOW CORNING 2503 is a stearyl dimethicone wax available from DowCorning, Midland, Mich.

The following tests were employed in evaluating the examples herein.

Test Method 1—Water Repellency

The water repellency of a treated substrate was measured according tothe DuPont Technical Laboratory Method as outlined in the TEFLON GlobalSpecifications and Quality Control Tests information packet. The testdetermines the resistance of a treated substrate to wetting by aqueousliquids. Drops of water-alcohol mixtures of varying surface tensions areplaced on the fabric and the extent of surface wetting is determinedvisually. The test provides a rough index of aqueous stain resistance.The higher the water repellency rating, the better the resistance thefinished substrate has to staining by water-based substances. Thecomposition of standard test liquids is shown in the following Table 1.Ratings of 0.5 increments are determined by subtracting one half fromthe numbers in Table 1 for borderline passing of the test liquid.

TABLE 1 Standard Test Liquids Water Repellency Composition Vol. %,Composition, Vol. % Rating Number Isopropyl Alcohol Distilled Water 1 298 2 5 95 3 10 90 4 20 80 5 30 70 6 40 60 7 50 50 8 60 40 9 70 30 10 8020 11 90 10 12 100 0

Test Method 2—Spray Rating

The dynamic water repellency of treated substrates was measuredaccording to the American Association of Textile Chemists and Colorists(AATCC) TM-22. Samples are visually scored by reference to publishedstandards, with a rating of 100 denoting no water penetration or surfaceadhesion. A rating of 90 denotes slight random sticking or wettingwithout penetration; lower values indicate progressively greater wettingand penetration. Test Method 2, the dynamic water repellency test, is ademanding and realistic test of water repellency.

Test Method 3—Wash Durability

Some fabric samples were laundered according to International Standardspecified domestic washing procedure for textile testing. Fabric sampleswere loaded into a horizontal drum, front-loading type (Type A, WASCATORFOM 71 MP-Lab) of automatic washing machine with a ballast load to givea total dry load of 4 lb. A commercial detergent was added (AATCC 1993standard Reference Detergent WOB) and the washer program ISO6330:2001-7A was used. After washing was complete, the entire load wasplaced into a KENMORE automatic dryer and dried on high for 45-50 min.

Test Method 4—Fabric Pre-Treatment

The fabrics treated in this study were 100% by weight khaki cotton twillavailable from SDL Atlas Textile Testing Solutions, Rock Hill, S.C.29732 and 100% by weight red polyester fabric available from L. MichaelOY, Finland. “New” fabrics were used without any pre-treatment method.

“Pre-washed” fabrics were washed in a KENMORE stackable washer/dryerwith 26.5 L washer capacity prior to application of the treatmentsolution. The washing machine was programmed for a small load and set torun a wash/rinse cycle with warm water. The wash cycle was started bysetting the dial to Heavy Duty Super and pulling the dial. The washbasin was allowed to completely fill, and 1993 AATCC Standard ReferenceDetergent WOB (19 g) was then added to the solution. Fabric samples werecharged into the wash basin, and the wash cycle was allowed to run tocompletion. The fabric was then placed into a KENMORE automatic dryerand dried on high for 40 minutes.

“Pre-treated” fabrics simulate textiles that have been treated using anindustrial method and washed multiple times by home washing methods. Thefabric was first treated with Urethane Dispersion 1 (UD1) polymer orwith a partially fluorinated polymethacrylic treating agent, CAPSTONE TC(available from DuPont Chemicals and Fluoroproducts, Wilmington, Del.)using a conventional aqueous pad bath (dipping) process at 30 g/L of thesolids content. For the treatment of the cotton fabric, a wetting agent,INVADINE PBN and a catalyzed cross-linking agent, KNITTEX 7636 (allavailable from Huntsman, Salt Lake City, Utah) were also included in thebath at 5 g/L and 30 g/L, respectively. The fabric was padded in thebath, and the excess liquid was removed by squeeze rollers. The wetpickup was around 95% on the cotton substrate. The “wet pick up” is theweight of the bath solution of the emulsion polymer and additivesapplied to the fabric, based on the dry weight of the fabric. The fabricwas cured at approximately 165° C. for 3 minutes and allowed to “rest”after treatment and cure for at least 2 hours. The treated fabrics had aspray rating of 100 (UD1) and 100 (CAPSTONE TC). The fabrics were thenwashed according to Test Method 3 to result in spray ratings of 70 (UD1)and 65 (CAPSTONE TC).

For the pre-treatment of the polyester fabric, a wetting agent,INVADINE® PBN (available from Huntsman, Charlotte, N.C., USA) and 60%acetic acid were also included in the bath at 5 g/L and 1 g/L,respectively. The fabric was padded in the bath, and the excess liquidremoved by squeeze rollers. The wet pickup was around 55% on thepolyester substrate. The “wet pick up” is the weight of the bathsolution of the emulsion polymer and additives applied to the fabric,based on the dry weight of the fabric. The fabric was cured atapproximately 160° C. for 2 minutes and allowed to “rest” aftertreatment and cure for about 15 to about 18 hours. The treated fabricshad a spray rating of 100 (UD1) and 100 (CAPSTONE TC). The fabrics werethen washed according to Test Method 3 to result in spray ratings of 70(UD1) and 75 (CAPSTONE TC).

Preparation of Urethane Dispersion 1 (UD1)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added sorbitan tristearate (519 g),sodium carbonate (3.2 g) and 4-methyl-2-pentanone (MIBK, 668 g). Afterthe solution was heated to 55° C., DESMODUR N100 (140 g) was added andthe temperature was increased to 80° C. Catalyst was added at 80° C. andreaction temperature was increased to 95° C. After 6 hours, n-butanol(8.2 g) and water (2.0 g) were added to the reaction mixture. Thefollowing morning, the reaction tested negative for active isocyanates,and 167.9 g of SILWAX D226 was added to the reaction mixture.

An aqueous dispersion of the compound was then prepared. Water (2336 g),CHEMIDEX S (18.3 g), ETHAL LA-4 (27.1 g), dipropylene glycol (207.0 g),and acetic acid (13.4 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C., and mineral oil(11.9 g) was added. The urethane reaction was cooled to 65° C., and thesurfactant solution was slowly added to produce a milky solution. Themixture was emersion blended (2 minutes), homogenized at 6000 psi, andthe resulting emulsion was distilled under reduced pressure to removethe solvent. An additional 8.6 g of CHEMIDEX S and 396 g of water wasadded to yield a non-flammable, cationic urethane dispersion at 25%solids after cooling and filtering.

Preparation of Urethane Dispersion 2 (UD2)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added sorbitan tristearate (259 g),sodium carbonate (1.6 g) and 4-methyl-2-pentanone (MIBK, 350 g). Afterthe solution was heated to 55° C., DESMODUR N100 (70 g) was added, andthe temperature was increased to 80° C. Catalyst was added at 80° C.,and the reaction temperature was increased to 95° C. After 6 hours,n-butanol (4.1 g) was added to the reaction mixture. The followingmorning, the reaction tested negative for active isocyanates, and 83.84g of SILWAX D226 was added to the reaction mixture.

An aqueous dispersion of the compound was then prepared. Water (2495 g)and WITCO C-6094 (52.9 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C., and 1.5 g ofWACKER SRE was added. The urethane reaction was cooled to 65° C., andthe surfactant solution was slowly added to produce a milky solution.The mixture was emersion blended (2 minutes), homogenized at 6000 psi,and the resulting emulsion was distilled under reduced pressure toremove the solvent and yield a non-flammable anionic urethane dispersionat 14% solids after cooling and filtering.

Preparation of Urethane Dispersion 3 (UD3)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added sorbitan tristearate (518 g),sodium carbonate (3.2 g) and 4-methyl-2-pentanone (MIBK, 858 g). Afterthe solution was heated to 55° C., DESMODUR N100 (140 g) was added, andthe temperature was increased to 80° C. Catalyst was added at 80° C.,and the reaction temperature was increased to 95° C. After 6 hours,n-butanol (8.2 g) and water (2.0 g) were added to the reaction mixture.

An aqueous dispersion of the compound was then prepared. Water (1884 g),CHEMIDEX S (14.6 g), ETHAL LA-4 (21.7 g), dipropylene glycol (165.8 g),and acetic acid (10.7 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C., and mineral oil(9.6 g) was added. The urethane reaction was cooled to 65° C., and thesurfactant solution was slowly added to produce a milky solution. Themixture was emersion blended (2 minutes), homogenized at 6000 psi, andthe resulting emulsion was distilled under reduced pressure to removethe solvent. An additional 6.6 g of CHEMIDEX S and 557 g of water wasadded to yield a non-flammable cationic urethane dispersion at 26%solids after cooling and filtering.

Preparation of Urethane Dispersion 4 (UD4)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added sorbitan tribehenin 50 (190.35 g),sodium carbonate (1.0 g) and 4-methyl-2-pentanone (MIBK, 233 g). Afterthe solution was heated to 55° C., DESMODUR N100 (45 g) was added andthe temperature was increased to 80° C. Catalyst was added at 80° C. andreaction temperature was increased to 95° C. After 6 hours, n-butanol(2.6 g) and water (0.6 g) were added to the reaction mixture.

An aqueous dispersion of the compound was then prepared. Water (673 g),CHEMIDEX S (5.2 g), ETHAL LA-4 (7.7 g), dipropylene glycol (58.9 g), andacetic acid (3.8 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C. and mineral oil(4.3 g) was added. The urethane reaction was cooled to 65° C. and thesurfactant solution was slowly added to produce a milky solution. Themixture was emersion blended (2 minutes), homogenized at 6000 psi, andthe resulting emulsion was distilled under reduced pressure to removethe solvent. An additional 2.2 g of CHEMIDEX S and 178 g of water wasadded to yield a non-flammable cationic urethane dispersion at 24%solids after cooling and filtering.

Preparation of Urethane Dispersion 5 (UD5)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added trioctyldodecyl citrate (175.13 g),sodium carbonate (1.15 g), and 4-methyl-2-pentanone (MIBK, 230 g). Afterthe solution was heated to 55° C., DESMODUR N100 (50 g) was added andthe temperature was increased to 80° C. Catalyst was added at 80° C.,and the reaction temperature was increased to 95° C. After 6 hours,n-butanol (3.0 g) and water (0.7 g) were added to the reaction mixture.

An aqueous dispersion of the compound was then prepared. Water (435 g),CHEMIDEX S (5.0 g), ETHAL LA-4 (7.4 g), dipropylene glycol (56.5 g), andacetic acid (3.6 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C. and mineral oil(3.3 g) was added. The urethane reaction was cooled to 65° C., and thesurfactant solution was slowly added to produce a milky solution. Themixture was filtered, blended, sonicated (2 minutes), and the resultingemulsion was distilled under reduced pressure to remove the solvent. Anadditional 1.91 g of CHEMIDEX S and 149 g of water was added to yield anon-flammable cationic urethane dispersion at 25% solids after coolingand filtering.

Preparation of Urethane Dispersion 6 (UD6)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added stearyl pentaerythitol (184.12 g),sodium carbonate (0.9 g) and 4-methyl-2-pentanone (MIBK, 220 g). Afterthe solution was heated to 55° C., DESMODUR N100 (40 g) was added andthe temperature was increased to 80° C. Catalyst was added at 80° C. andreaction temperature was increased to 95° C. After 6 hours, n-butanol(2.4 g) and water (0.6 g) were added to the reaction mixture.

An aqueous dispersion of the compound was then prepared. Water (644 g),CHEMIDEX S (5.0 g), ETHAL LA-4 (7.3 g), dipropylene glycol (56.0 g), andacetic acid (3.6 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C. and mineral oil(4.0 g) was added. The urethane reaction was cooled to 65° C. and thesurfactant solution was slowly added to produce a milky solution. Themixture was emersion blended (2 minutes), homogenized at 6000 psi andthe resulting emulsion was distilled under reduced pressure to removethe solvent. An additional 2.0 g of CHEMIDEX S and 100 g of water wasadded at 65° C. to yield a non-flammable urethane dispersion at 24%solids after cooling and filtering.

Preparation of Wax Dispersion 1 (WD1) Into a 4-neck round bottom flaskequipped with an overhead stirrer, thermocouple and condenser was addedDOW CORNING 2503 cosmetic wax (100 g) and MIBK (250 g). The solution washeated to 65° C.

An aqueous dispersion of the compound was then prepared. Water (507 g),CHEMIDEX S (2.2 g), ETHAL LA-4 (3.2 g), dipropylene glycol (24.6 g), andacetic acid (1.6 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C. The wax solutiontemperature was increased to 65° C. and the surfactant solution wasslowly added to produce a milky solution. The mixture was blended withexcess water, homogenized at 6000 psi and the resulting emulsion wasdistilled under reduced pressure to remove the solvent. An additional0.6 of CHEMIDEX S was dissolved at 65° C. after distillation to yield anon-flammable cationic dispersion at 7.56% solids after cooling andfiltering.

Preparation of Wax Dispersion 2 (WD2)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added WACKER W23 (100 g) and MIBK (250g). The solution was heated to 65° C.

An aqueous dispersion of the compound was then prepared. Water (782 g),CHEMIDEX S (2.2 g), ETHAL LA-4 (2.8 g), dipropylene glycol (24.6 g), andacetic acid (1.5 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C. The wax solutiontemperature was increased to 65° C. and the surfactant solution wasslowly added to produce a milky solution. The mixture was blended withexcess water, homogenized at 6000 psi, and the resulting emulsion wasdistilled under reduced pressure to remove the solvent. An additional0.7 of CHEMIDEX S was dissolved at 65° C. after distillation to yield anon-flammable cationic dispersion at 12% solids after cooling andfiltering.

Preparation of Wax Dispersion 3 (WD3)

Into a 4-neck round bottom flask equipped with an overhead stirrer,thermocouple and condenser was added SILTECH E1316 (100 g) and MIBK (250g). The solution was heated to 65° C.

An aqueous dispersion of the compound was then prepared. Water (782 g),CHEMIDEX S (2.2 g), ETHAL LA-4 (2.8 g), dipropylene glycol (24.6 g), andacetic acid (1.5 g) were added to a beaker and stirred to form asurfactant solution. The solution was heated to 65° C. The wax solutiontemperature was increased to 65 C and the surfactant solution was slowlyadded to produce a milky solution. The mixture was blended, homogenizedat 6000 psi and the resulting emulsion was distilled under reducedpressure to remove the solvent. An additional 0.6 of CHEMIDEX S wasdissolved at 65° C. after distillation to yield a non-flammable cationicdispersion at 12% solids after cooling and filtering.

Comparative Example A Untreated Fabric

Untreated (new) fabric samples were tested according to Test Methods 1and 2.

TABLE 2 Performance of Comparative Example A Cotton Polyester Water DropRating 0 0 Spray Rating 0 0

Example 1 Performance of UD1 in Wash and Rinse Cycles

A KENMORE stackable washer/dryer with 26.5 L washer capacity wasprogrammed for a small load and set to run a wash and rinse cycle withhot or cold water according to Table 3. UD1 (795.00 g) was mixed in abeaker with a wetting agent (INVADINE PBN, 132.0 g). The wash cycle wasstarted by setting the dial to Heavy Duty Super and pulling the dial.The water was allowed to partially fill the wash basin, and the urethanedispersion mixture was charged into the wash basin. The wash basin wasallowed to completely fill, yielding an aqueous solution having 30 g/Lof urethane compound (solids). Fabric samples were charged into the washbasin, and the wash cycle was allowed to run to completion.

The fabric was placed into a KENMORE automatic dryer and dried on highfor 40 minutes (1^(st) Dry). Internal dryer temperature was measuredduring the 1^(st) Dry to be 60° C. The fabric was placed back into aKENMORE automatic dryer and dried on high for an additional 40 minutes(2^(nd) Dry). Internal dryer temperature was measured during the 2^(nd)Dry to be 75° C. The fabric samples were allowed to sit for at least 2hours and were then tested according to Test Methods 1 and 2.

TABLE 3 Performance of Example 1 Hot Wash and Cold Cold Wash and ColdRinse Rinse Cotton Polyester Cotton Polyester Water Drop Rating 1^(st)Dry (New) 3 3 3 3 2^(nd) Dry (New) 3 3 3 3 1^(st) Dry (Pre-washed) 3 3 33 2^(nd) Dry (Pre-washed) 3 3 3 3 Spray Rating 1^(st) Dry (New) 90 10070 100 2^(nd) Dry (New) 95 100 95 100 1^(st) Dry (Pre-washed) 85 100 85100 2^(nd) Dry (Pre-washed) 100 100 90 95

The performance data of Table 3 demonstrates the efficacy of theinventive process to provide water repellency to a fabric when usedduring the wash cycle of a washing machine. Superior water repellencywas achieved on both cotton and polyester fabrics, either new orpre-washed, using either hot or cold wash cycles.

Example 2 Performance of UD1 in Rinse Cycle

Example 1 was repeated, except the KENMORE washer was programmed for aHeavy Duty Rinse cycle at warm or cold temperatures according to Table4.

TABLE 4 Performance of Example 2 Warm Rinse Cold Rinse Cotton PolyesterCotton Polyester Water Drop Rating 1^(st) Dry (New) 3 3 3 3 2^(nd) Dry(New) 3 3 3 3 1^(st) Dry (Pre-washed) 3 3 3 3 2^(nd) Dry (Pre-washed) 33 3 3 1^(st) Dry (Pre-treated 4 4 4 4 with UD1) 1^(st) Dry (Pre-treated5 7 8 7 with CAPSTONE TC) Spray Rating 1^(st) Dry (New) 90 100 100 1002^(nd) Dry (New) 95 100 100 100 1^(st) Dry (Pre-washed) 80 90 100 1002^(nd) Dry (Pre-washed) 85 100 100 100 1^(st) Dry (Pre-treated 100 100100 100 with UD1) 1^(st) Dry (Pre-treated 75 100 100 100 with CAPSTONETC)

The performance data of Table 4 demonstrates the efficacy of theinventive process to provide water repellency to a fabric when usedduring the rinse cycle of a washing machine. Superior water repellencywas achieved on both cotton and polyester fabrics, either new orpre-washed, using either hot or cold wash cycles. Additionally, theprocess was shown to increase the spray ratings of fabrics that had beenpre-treated and washed, indicating that the process can be used torestore water repellency to worn treated fabrics.

Example 3 Performance of UD2 in Wash Cycles with Detergent, and RinseCycles without Detergent

A KENMORE stackable washer/dryer with 26.5 L washer capacity wasprogrammed for a small load and set to run a wash/rinse or rinse cyclewith hot or cold water according to Table 5. UD2 (1400.00 g) was mixedin a beaker with a wetting agent (INVADINE PBN, 132.0 g). The wash orrinse cycle was started by setting the dial to Heavy Duty Super (Wash)or Heavy Duty Rinse (Rinse), respectively, and pulling the dial. Thewater was allowed to partially fill the wash basin, and the urethanedispersion mixture was charged into the wash basin. The wash basin wasallowed to completely fill, yielding an aqueous solution having 30 g/Lof urethane compound (solids). For the wash cycles, 1993 AATCC StandardReference Detergent WOB (19 g) was then added to the solution. Fabricsamples were charged into the wash basin, and the wash cycle was allowedto run to completion.

The fabric was placed into a KENMORE automatic dryer and dried on highfor 40 minutes (1^(st) Dry). Internal dryer temperature was measuredduring the 1st Dry to be 60° C. The fabric was placed back into aKENMORE automatic dryer and dried on high for an additional 40 minutes(2^(nd) Dry). Internal dryer temperature was measured during the 2^(nd)Dry to be 75° C. The fabric samples were allowed to sit for at least 2hours and were then tested according to Test Methods 1 and 2.

TABLE 5 Performance of Example 3 Hot Wash and Cold Wash and Cold RinseCold Rinse Cold Rinse Cot- Poly- Cot- Poly- Cot- Poly- ton ester tonester ton ester Water Drop Rating 1^(st) Dry 0 4 0 4 4 3 (New) 2^(nd)Dry 1 4 0 4 4 3 (New) Spray Rating 1^(st) Dry 0 100 0 80 85 85 (New)2^(nd) Dry 25 100 0 85 85 85 (New)

The performance data of Table 5 demonstrates the efficacy of an anionicsystem to provide water repellency to a fabric when used in combinationwith a detergent or during the rinse cycle of a washing machine. Whenthe treating agent was used in combination with a detergent during awash cycle, the polyester fabric substrates exhibited superior waterrepellency. Additionally, the process was shown to increase the waterrepellency of both cotton and polyester fabrics when used during a rinsecycle without detergent.

Example 4 Performance of UD3 in a Cold Rinse Cycle

A KENMORE stackable washer/dryer with 26.5 L washer capacity wasprogrammed for a small load and set to run a rinse cycle with coldwater. UD3 (760.00 g) was mixed in a beaker with a wetting agent(INVADINE PBN, 132.0 g). The wash cycle was started by setting the dialto Heavy Duty Rinse and pulling the dial. The water was allowed topartially fill the wash basin, and the urethane dispersion mixture wascharged into the wash basin. The wash basin was allowed to completelyfill, yielding an aqueous solution having 30 g/L of urethane compound(solids). Fabric samples were charged into the wash basin, and the washcycle was allowed to run to completion.

The fabric was placed into a KENMORE automatic dryer and dried on highfor 40 minutes (1^(st) Dry). Internal dryer temperature was measuredduring the 1^(st) Dry to be 60° C. The fabric was placed back into aKENMORE automatic dryer and dried on high for an additional 40 minutes(2^(nd) Dry). Internal dryer temperature was measured during the 2^(nd)Dry to be 75° C. The fabric samples were allowed to sit for at least 2hours and were then tested according to Test Methods 1 and 2.

Example 5 Performance of UD3/WD1 Blend in a Cold Rinse Cycle

Example 4 was repeated, except that both UD3 (608.00 g) and WD1 (520.00g) were used.

Example 6 Performance of UD3/WD2 Blend in a Cold Rinse Cycle

Example 4 was repeated, except that both UD3 (608.00 g) and WD2 (322.00g) were used.

Example 7 Performance of UD3/WD3 Blend in a Cold Rinse Cycle

Example 4 was repeated, except that both UD3 (608.00 g) and WD3 (314.00g) were used.

TABLE 6 Performance of Examples 4-7 Ex. 4 5 6 7 Cot- Poly- Cot- Poly-Cot- Poly- Cot- Poly- ton ester ton ester ton ester ton ester Water DropRating 1^(st) Dry 3 3 3 3 3 3 3 3 (New) Spray Rating 1^(st) Dry 80 90 85100 70 100 90 100 (New)

The performance data of Table 6 demonstrates the efficacy of differentblend compositions to provide water repellency to a fabric when usedduring the rinse cycle of a washing machine. The process, using variedtreating compositions, was shown to provide excellent water repellencyto both cotton and polyester fabrics.

Example 8 Performance of UD4 in a Cold Rinse Cycle

Example 4 was repeated, except that UD4 (828.00 g) was used.

Example 9 Performance of UD5 in a Cold Rinse Cycle

Example 4 was repeated, except that UD5 (792.00 g) was used.

Example 10 Performance of UD6 in a Cold Rinse Cycle

Example 4 was repeated, except that UD6 (818.00 g) was used.

TABLE 7 Performance of Examples 8-10 Ex. 8 9 10 Cot- Poly- Cot- Poly-Cot- Poly- ton ester ton ester ton ester Water Drop Rating 1^(st) Dry 33 0 1 3 3 (New) Spray Rating 1^(st) Dry 80 100 0 50 80 100 (New)

The performance data of Table 7 demonstrates the efficacy of differenttreating compositions to provide water repellency to a fabric when usedduring the rinse cycle of a washing machine. The process, using variedurethane compounds, was shown to provide excellent water repellency tofibrous substrates.

The compositions, methods, and substrates of the present invention areuseful to provide excellent water repellency and optionally stainrelease to treated substrates by application in the home or small-scaleenvironment. Because the method can be used to provide surfaceproperties to treated or untreated fabrics, the consumer has the abilityto enhance performance of a previously untreated substrate, or boostperformance of a previously treated but worn substrate. The use ofnon-fluorinated organic urethane have been found to provide superiorwater repellency and durable water repellency compared to traditionalnon-fluorinated water repellents and are comparable to commerciallyavailable fluorinated water repellents. The treated substrates of thepresent invention are useful in a variety of applications and productssuch as clothing, bedding, protective garments, rugs, upholstery,furnishings, and other uses. The excellent surface properties describedabove help to maintain surface cleanliness and therefore can permitlonger use.

What is claimed is:
 1. A method of imparting water repellency andoptionally stain release to fibrous substrates comprising contacting afibrous substrate with a laundry treatment composition inside a laundrymachine, wherein the laundry treatment composition comprises ahydrophobic compound having at least one linkage of Formula I:NHC(O)—X—  (I) wherein X is the residue of a cyclic or acyclic sugaralcohol which is substituted with at least one —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; or mixtures thereof; where thecyclic or acyclic sugar alcohol is selected from a saccharide, reducedsugar, aminosaccharide, aldonic acid, or aldonic acid lactone; whereineach n is independently 0 to 20; each m is independently 0 to 20; m+n isgreater than 0; each R¹ is independently a linear or branched alkylgroup having 5 to 29 carbons optionally comprising at least 1unsaturated bond; and each R² is independently —H, a linear or branchedalkyl group having 6 to 30 carbons optionally comprising at least 1unsaturated bond, or mixtures thereof.
 2. The method of claim 1 whereinX is at least 50% bio-based derived.
 3. The method of claim 1 wherein Xis 100% bio-based derived.
 4. The method of claim 1 wherein X isselected from Formulas (IIa), (IIb), or (IIc):

wherein each R is independently a direct bond to NHC(O) of Formula I;—H; —R¹; —C(O)R¹; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; each n is independently 0 to 20;each m is independently 0 to 20; m+n is greater than 0; r is 1 to 3; ais 0 or 1; p is independently 0 to 2; provided that a is 0 when r is 3;each R¹ is independently a linear or branched alkyl group having 5 to 29carbons optionally comprising at least 1 unsaturated bond; each R² isindependently —H, a linear or branched alkyl group having 6 to 30carbons optionally comprising at least 1 unsaturated bond; or mixturesthereof, provided when X is Formula (IIa), then at least one R is adirect bond to NHC(O) of Formula 1; and at least one R is a —R¹;—C(O)R¹; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; each R⁴ is independently a directbond to NHC(O) of Formula I; —H, a linear or branched alkyl group having6 to 30 carbons optionally comprising at least 1 unsaturated bond, orcombinations thereof; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; provided when X is Formula (IIb),then at least one R or R⁴ is a direct bond to NHC(O) of Formula 1; andat least one R or R⁴ is a linear or branched alkyl group optionallycomprising at least 1 unsaturated bond, or combinations thereof;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; and each R¹⁹ is a direct bond toNHC(O) of Formula I; —H, —C(O)R¹, or —CH₂C[CH₂OR]₃, provided when X isFormula (IIc), then at least one R¹⁹ or R is a direct bond to NHC(O) ofFormula I; and at least one R¹⁹ is —C(O)R¹,—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹.
 5. The method of claim 1, whereinthe hydrophobic compound further comprises at least one moiety Q to formFormula (I′):-Q-NHC(O)—X—  (I′) where Q is a monovalent, divalent, or polyvalentmoiety selected from linear or branched, cyclic or acyclic, alkylenegroups optionally containing at least one group selected from alkoxy,phenyl, siloxane, urethane, urea, biuret, uretdione, cyclizedisocyanate, allophanate, or isocyanurate.
 6. The method of claim 1,wherein the hydrophobic compound further comprises at least one linkageselected from Formulas (IVa), (IVb), (IVc), or mixtures thereof:R⁶-D  (IVa),R¹⁵—(OCH₂CH(OR¹⁶)CH₂)_(z)—OR¹⁷  (IVb),—NH—C(O)—NH—X  (IVc) wherein D is selected from —N(R¹²)—C(O)—NH—,—OC(O)NH—, —C(O)NH—, —SC(O)NH—,—O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—C(O)NH—, or—[C(O)]—O—(CH₂CH₂O)_(s)(CH(CH₃)CH₂O)_(t)—C(O)NH—; X is defined as above;R⁶ is selected from a —C₁ to C₃₀ linear or branched alkyl optionallycomprising at least one unsaturated group, a hydroxy- orurethane-functional C₁ to C₃₀ linear or branched alkyl, a hydroxy- orurethane-functional linear or branched C₁ to C₃₀ polyether, a hydroxy-or urethane-functional linear or branched polyester having a polyesterpolymer backbone, a hydroxy- or urethane-functional linear or branchedorganosiloxane, an amine- or urea-functional linear or branchedorganosiloxane, a thiol- or thiocarbonate functional C₁ to C₃₀ linear orbranched alkyl, an amine- or urea-functional C₁ to C₃₀ linear orbranched alkyl

wherein R⁷, R⁸, and R⁹ are each independently, —H, —C₁ to C₆ alkyl, orcombinations thereof; R¹⁰ is a divalent alkyl group of 1 to 20 carbons;R¹² is —H or a monovalent C₁ to C₆ alkyl group; R¹⁵, R¹⁶, and R¹⁷ areeach independently a —H; —C(O)NH—, —R¹⁸; —C(O)R¹⁸ provided that at leastone R¹⁵, R¹⁶, or R¹⁷ is a —C(O)NH—; R¹⁸ is independently a linear orbranched alkyl group having 5 to 29 carbons optionally comprising atleast 1 unsaturated bond; z is 1 to 15; Y is Cl; s is an integer of 0 to50; t is an integer of 0 to 50; and s+t is greater than
 0. 7. The methodof claim 4 wherein X is selected from Formula (IIa) to be Formula(IIa′):

wherein R is further limited to independently a direct bond to NHC(O),—H; —R¹; or —C(O)R¹.
 8. The method of claim 4 wherein X is selected fromFormula (IIa) to be Formula (IIa′):

wherein R is further limited to independently a direct bond to NHC(O),—H; —(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²; or—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹.
 9. The method of claim 1 whereinX is selected from Formula (IIb).
 10. The method of claim 1 wherein X isselected from Formula (IIc).
 11. The method of claim 1, where thelaundry treatment composition further comprises a wax.
 12. The method ofclaim 11, where the wax is selected from beeswax; microcrystalline wax;oxidized microcrystalline wax; paraffin wax; montan wax; ozokerite wax;carnauba wax; candililla wax; palm wax; whale wax; lanolin; sugar canewax; sugar esters; polyolefin wax; mono-, di, or tri-glyceride esters;fatty acid ester waxes; or blends thereof.
 13. The method of claim 1wherein the contacting step occurs during a laundry machine wash cycleor rinse cycle.
 14. The method of claim 1 wherein the fibrous substrateis contacted prior to starting a laundry machine wash cycle or rinsecycle.
 15. The method of claim 1 further comprising a step of curing thehydrophobic compound with heat.
 16. The method of claim 15, where thestep of curing is completed by machine drying in a dryer, ironing,steaming, blow drying, drying under a heat lamp, or drying near aradiative source of heat.
 17. A substrate treated according to themethod of claim
 1. 18. A laundry additive composition comprising a firstlaundry treatment composition and a second laundry treatment compositionwhich is different than the first laundry treatment composition, wherethe first laundry treatment composition comprises a hydrophobic compoundhaving at least one linkage of Formula I:NHC(O)—X—  (I) wherein X is the residue of a cyclic or acyclic sugaralcohol which is substituted with at least one —R¹; —C(O)R¹;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)R²;—(CH₂CH₂O)_(n)(CH(CH₃)CH₂O)_(m)C(O)R¹; or mixtures thereof; where thecyclic or acyclic sugar alcohol is selected from a saccharide, reducedsugar, aminosaccharide, aldonic acid, or aldonic acid lactone; whereineach n is independently 0 to 20; each m is independently 0 to 20; m+n isgreater than 0; each R¹ is independently a linear or branched alkylgroup having 5 to 29 carbons optionally comprising at least 1unsaturated bond; each R² is independently —H, a linear or branchedalkyl group having 6 to 30 carbons optionally comprising at least 1unsaturated bond, or mixtures thereof.
 19. The laundry additivecomposition of claim 18, comprising the hydrophobic compound in anamount of 0.001% to 10% by weight of the total composition.
 20. Thelaundry additive composition of claim 19, where the second laundrytreatment composition is a laundry detergent composition, fabricsoftener composition, wrinkle release agent, stain release agent,bleaching agent, or color brightening agent.